Film PETG de înaltă durabilitate
Film PETG de înaltă durabilitate is a thermoplastic polyester film based on polyethylene terephthalate glycol-modified resin. The glycol modification reduces the crystallization tendency of standard PET, producing an amorphous sheet with higher impact resistance and better thermoforming range. The film is supplied in thicknesses from 0.25 mm to 6.0 mm, in widths up to 2.1 m, with clear, colored, and frosted surface options. Impact strength reaches 8 to 12 kJ/m² by Charpy notched testing, and the film resists crazing under repeated flexural loading. High Durability PETG Film is specified for machine guards, signage, protective barriers, and thermoformed components where optical clarity and impact resistance are required together over a long service period.
Program de film personalizat
Film PETG de înaltă durabilitate is supplied under an ODM/OEM arrangement. Thickness, width, surface finish, color, and cut format are set according to the buyer's drawing or performance brief. Clear and tinted grades, matte and anti-glare surfaces, and hard-coated variants are developed and documented against a single approved specification sheet, and the approved sheet governs every production lot.
Profil de performanță
Absorbția energiei de impact
Film PETG de înaltă durabilitate absorbs impact energy through ductile deformation rather than brittle fracture. Charpy notched impact values of 8 to 12 kJ/m² are maintained at temperatures from -20°C to 40°C, so the film retains its protective function in outdoor and cold-storage installations where acrylic sheet cracks.
Rezistenta la oboseala la incovoiere
Structura amorfă a filmului tolerează îndoirea repetată fără albire prin stres. Testarea la oboseală la încovoiere conform ASTM D671 nu returnează nicio inițiere a fisurilor după 100.000 de cicluri la o amplitudine de deformare de 0,5%, susținând utilizarea în dispozitive de protecție cu balamale, dispozitive de afișare și panouri de barieră flexibile.
Claritate optică
Filmele PETG de înaltă durabilitate transmit 84% până la 90% din lumina vizibilă cu valori de ceață sub 1,0%. Suprafața nu îngălbenește la iluminarea interioară pe o perioadă de 10 ani, iar gradele stabilizate la UV mențin schimbarea culorii în Delta E 2.0 sub 2.000 de ore de intemperii accelerate.
Rezistență chimică și de curățare
Filmul rezistă la curățați alcalini diluați, detergenți neutri și dezinfectanți pe bază de alcool. Rezistența la solvenți aromatici și cetone este limitată; agenții de curățare bazați pe acele chimie îndepărtează luciul de suprafață și sunt excluși din protocolul de întreținere.
Gama de termoformare
Film PETG de înaltă durabilitate forms at 120°C to 160°C with a wide processing window. Deep draws and complex shapes are produced without pre-drying, and the formed part retains impact resistance at the stretched corners. Mold shrinkage is 0.2% to 0.6%, consistent across production runs.
Stabilitate dimensională
Filmul își păstrează dimensiunile tăiate în timpul schimbărilor de umiditate de la 20% la 80% umiditate relativă. Expansiunea termică liniară este de 6,5 x 10⁻⁵ per °C, comparabilă cu aluminiul, ceea ce simplifică proiectarea cadrului în cazul în care filmul este montat între extruziunea metalică.
Date tehnice
Câmpuri de aplicare
Întrebări despre cumpărător
Cum se compară PETG cu acrilul pentru aplicații de impact?
Film PETG de înaltă durabilitate provides higher impact resistance than cast acrylic at the same thickness, with Charpy notched values of 8 to 12 kJ/m² against typical acrylic values below 2 kJ/m². Acrylic offers higher surface hardness and better scratch resistance. For barrier and guard applications, PETG is specified; for high-scratch display faces, acrylic or a hard-coated PETG grade is preferred.
Este necesară uscarea înainte de termoformare?
Film PETG de înaltă durabilitate does not require pre-drying in the normal shop environment. The film absorbs less than 0.2% moisture at 50% relative humidity, and that moisture level does not cause surface defects during forming. If the film has been stored in high humidity for an extended period, a 2-hour dry cycle at 65°C is recommended before forming thick-gauge sheet above 4.0 mm.
Ce metode de tăiere și finisare a muchiei sunt potrivite?
Filmul este tăiat cu router CNC, laser, ferăstrău sau tăiere cu matriță. Tăierea cu laser lasă o margine lustruită, dar poate produce o ușoară nuanță de chihlimbar la linia de tăiere; Direcționarea CNC cu un bit ascuțit cu un singur canal produce o margine curată. Lustruirea marginilor cu o flacără sau un șervețel cu solvent îndepărtează urmele routerului și clarifică marginea pentru aplicații vizibile.
Cum ar trebui să fie curățată filmul în timpul serviciului?
Curățați cu o cârpă moale și o soluție de detergent neutru sau un dezinfectant pe bază de alcool. Clătiți cu apă curată și uscați cu o cârpă din microfibră. Nu utilizați detergenți pentru sticlă pe bază de amoniac, acetonă sau tampoane abrazive, care atacă suprafața și reduc claritatea. Pentru tipurile de acoperire dur, urmați instrucțiunile de întreținere ale furnizorului de acoperire.
Filmul poate fi lipit de alte materiale?
Film PETG de înaltă durabilitate bonds to rigid substrates with solvent-free PU adhesive, acrylic adhesive tape, or structural acrylic adhesive. Solvent-based adhesives containing ketones or aromatic solvents attack the film surface and cause crazing. Test coupon bonding should be completed before production, particularly where the assembly will be exposed to temperature cycling.
Note de manipulare și depozitare
- Depozitați foile de film PETG de înaltă durabilitate pe un palet rigid, într-o zonă uscată, la 10°C până la 30°C. Nu sprijiniți cearșafurile de un perete pentru perioade lungi de timp; cearşaful se poate înclina sub propria greutate.
- Păstrați filmul de mascare de protecție pe loc în timpul tăierii și manipulării pentru a preveni zgârieturile la suprafață. Îndepărtați mascarea în 30 de zile de la livrare pentru a evita transferul adezivului pe suprafața filmului.
- Curățați filmul cu o cârpă moale și detergent neutru. Tampoanele abrazive, detergenții pe bază de amoniac și produsele pe bază de solvenți care conțin cetone sau aromatice daunează suprafeței.
- Sprijiniți întreaga zonă a foii în timpul transportului și instalării. Marginile nesuportate ale tablei de ecartament subțire se pot deforma și crăpa atunci când sunt ridicate într-un singur punct.
- Pentru instalațiile în aer liber, specificați gradul stabilizat la UV și confirmați că sistemul de fixare permite o dilatare termică de 6,5 x 10⁻⁵ per °C fără a constrânge marginea panoului.